Ring Permanent Sintered NdFeB Iron Boron Magnet Used in Packing
|FOB Price:||Get Latest Price|
|Min. Order:||10 Pieces|
|Production Capacity:||1000 Ton/Year|
|Payment Terms:||T/T, Western Union, Paypal|
- Model NO.: N40
- Shape: Ring
- Grade: N42
- Material: Neodymium, Iron and Boron
- Working Temperature: Max. 80
- Transport Package: Packed in Plastic Then Put in Cartons
- Origin: China
- Application: Speaker Magnet, Industrial Magnet, Motor Magnet
- Coating: Nickel
- Type: Permanent
- Density: 7.5g/cm3
- Trademark: TSL
- Specification: rosh
- HS Code: 7202991900
Need other size of NdFeB Iron Boron Magnet and more information,please feel free to contact us.
Sintered NdFeB Iron Boron Magnets are composed of Neodymium, Iron and Boron. Density of NdFeB Iron Boron Magnet is. 27Lb/in3 (7.5g/cm3).
NdFeB Iron Boron Magnet are manufactured in a metallurgy process through alloying, crushing, powdering, pressing w/magnetic orientation, sintering, then cutting, coating, inspecting and packing before shipment.
Sintered NdFeB Iron Boron Magnet offer the highest (BH)max and high Hci(BH)max, the Maximum Energy Product, of Neodymium magnets is highest of any kind of permanent magnets today in the world. (BH)max at different grades of Neodymium magnets is 27 to 52 MGOe. Neodymium magnets have extremely resistance to demagnetization with Hci, Intrisic coercive force, over 12, 000 Oe. Because of very high (BH)max and Hci, Neo magnets could be used as a reversible medium for large amount of energy transformation in miniaturized application where a strong magnetic demagnetization field exists, such as computer hard drive. Disk and rectangle shapes for customers' immediate needs and accept special orders for custom Neodymium magnets.
Sintered NdFeB Iron Boron Magnet are most powerful of any kind of magnetic materialsBr of Neodymium magnets are much more than 11, 000 Gauss. Therefore, Neodymium magnets have strong holding strength on metal surface and could be used as component for holding, separating, etc. Neodymium magnets must be carefully handled to avoid personal injury and material damage due to its extremely magnetic strength and brittle property.
NdFeB Iron Boron Magnet are sensitive to temperature change and even lose magnet properties at high temperatureNeodymium magnets lose -0.09 ~ -0.13% of Br/° C and can work stably under 80° C for low Hci Neodymium magnets and 150° C for high Hci Neodymium magnets.
NdFeB Iron Boron Magnet are corrupted in humid environment Surface protection is strongly recommended, such as plating, varnishing and encapsulating.
Sintered NdFeB Iron Boron Magnet are hard and brittle Neodymium magnets can be abrasively machined with coolant served to absorb heating and dust. Without coolant, rare earth magnets could crack and chip by the heat produced during high speed cutting or grinding, and the sparks contain the easily oxidized grinding dust that could cause fire!
Magnetic Property of NdFeB Iron Boron Magnet
RingOuter Radius*Inner Radius*Thickness*
Maximum150.0 mm95.0 mm50.0 mm
Minimum0.8 mm0.15 mm0.2 mm
Maximum150.0 mm75.0 mm
Minimum0.4 mm0.25 mm
Maximum200.0 mm95.0 mm50.0 mm150.0 mm
Minimum3.080 mm1.20 mm0.25 mm0.50 mm
Arc-segmentOuter Radius*Inner Radius*Thickness*Degree*
Maximum75 mm65 mm50.00 mm150